The present invention relates to a steel sheet that consists essentially of
0.10 to 0.37% C, 1% or less Si, 2.5% or less Mn, 0.1% or less P, 0.03% or
less S, 0.01 to 0.1% sol.Al, 0.0005 to 0.0050% N, 0.0003 to 0.0050% B, by
mass, and balance of Fe, [14B/(10.8N)] being 0.5 or more, average particle
size of precipitate BN being 0.1 .mu.m or more, and grain size of prior
austenite after the hardening treatment being 2 to 25 .mu.m. The steel
sheet according to the present invention allows an inexpensive hardening
treatment method to be applied to improve the strength to a level required
for the structural components and the functional components of
automobiles, while providing excellent toughness after the hardening
treatment.
A invenção atual relaciona-se a uma folha de aço que consista essencialmente em 0.10 a 0.37% C, 1% ou menos 2.5% ou a menos do manganês, 0.1% ou a menos de P, 0.03% ou menos S do silicone, 0.01 a 0.1% sol.Al, 0.0005 a 0.0050% N, 0.0003 a 0.0050% B, pela massa, e pelo contrapeso do Fe, [ 14B/(10.8N) ] sendo 0.5 ou mais, o tamanho de partícula médio dos BN do precipitate que são 0.1 mu.m ou mais, e o tamanho de grão do austenite prévio após o tratamento endurecendo-se que é o mu.m 2 a 25. A folha de aço de acordo com a invenção atual permite que um método de tratamento endurecendo-se barato seja aplicado para melhorar a força a um nível requerido para os componentes estruturais e os componentes funcionais dos automóveis, ao fornecer o toughness excelente após o tratamento endurecendo-se.