Polyester multi-filamentary yarn, useful as tire reinforcement, is produced
by melting polyester resin at 290.degree. C. or below including at least
90 mol % of polyethylene terephthalate with intrinsic viscosity of
0.7-1.2; filtering the molten resin for filtering retention time of ten
minutes or below; spinning the filtered, molten resin by extrusion through
a nozzle which has 250-500 holes, each ranging in diameter from 0.5 mm to
1.2 mm with a length/diameter ratio from 2 to 5; primarily quenching the
extruded yarn at a temperature of 100-195.degree. C. in a zone of 50 mm or
more distance directly below the nozzle; secondarily quenching the yarn
with air at its glass transition temperature (Tg) or below; taking off the
yarn at spinning stress of 0.3 g/d or greater; drawing taken-off yarn at
total draw ratio of 1.3 or greater; and thermally treating the yarn at
temperature 150-230.degree. C.
El hilado multi-multi-filamentary del poliester, útil como refuerzo del neumático, es producido derritiendo la resina del poliester en 290.degree. C. o debajo de incluir por lo menos 90 mol de % de terephthalate del polietileno con la viscosidad intrínseca de 0.7-1.2; filtración de la resina fundida por el tiempo de filtración de la retención de diez minutos o abajo; haciendo girar haber filtrado, resina fundida por la protuberancia a través de un inyector que tiene 250-500 agujeros, cada uno que se extiende en diámetro a partir de 0.5 milímetro a 1.2 milímetros con un cociente de length/diameter a partir del 2 a 5; sobre todo apagar el hilado sacado en una temperatura de 100-195.degree. C. en una zona de 50 milímetros o de más distancia directamente debajo del inyector; secundario apagar el hilado con aire en su temperatura de transición de cristal (Tg) o abajo; sacar el hilado en la tensión que hace girar de 0.3 g/d o mayor; hilado tomado -apagado en el cociente total del drenaje de 1.3 o mayor de dibujo; y termal tratando el hilado en la temperatura 150-230.degree. C.