The present invention is directed to a corrosion and erosion resistant High
Chromium, Nitrogen bearing alloy, comprising the following composition in
wt. %: 28-48 chromium, 0.01-0.7 nitrogen, 0.5-30 manganese, 0.01-5 boron,
0.3-2.5 carbon, up to 0.01-25 cobalt plus nickel, up to 0.01-5 silicon, up
to 0.01-8 copper, up to 0.01-6 molybdenum, up to 2% of each one selected
from group consisting of zirconium, vanadium, cerium, titanium, tungsten,
niobium, aluminum, calcium, and rare earth elements with the balance being
essentially iron and other trace elements or inevitable impurities. The
alloy has a microstructure comprising hypoeutectic, eutectic, chromium
carbides, boride and nitrides in the austenitic matrix, saturated with
nitrogen with virtually no secondary carbides and nitrides.
La presente invenzione è diretta verso una corrosione e bicromato di potassio resistente di erosione alto, lega del cuscinetto dell'azoto, contenente la seguente composizione nei pesi %: il bicromato di potassio 28-48, 0.01-0.7 azoti, 0.5-30 manganesi, 0.01-5 boro, 0.3-2.5 carbonio, fino a 0.01-25 cobalti più nichel, fino a 0.01-5 siliconi, fino a 0.01-8 rami, fino a 0.01-6 molibdeno, fino a 2% di ogni scelto dallo zirconio consistente del gruppo, vanadio, cerio, titanio, tungsteno, niobio, alluminio, calcio ed elementi della terra rara con l'equilibrio che è essenzialmente rivestono di ferro ed altri oligoelementi o impurità inevitabili. La lega ha i carburi hypoeutectic, eutettici, del bicromato di potassio contenere di microstruttura, un boride e nitruri nella tabella austenitica, saturata con azoto con virtualmente nessun carburi e nitruri secondari.