Nano-sized particles such as nano-clays can be mixed with polymers through
either melt compounding or in-situ polymerization. By modifying the
particle surface with various surfactants and controlling processing
conditions, we are able to achieve either intercalated (partial
dispersion) or exfoliated (full dispersion) nano-clay distribution in
polymers with the clay content up to 35% by weight. When a blowing agent
is injected into the nanocomposite in an extruder (a continuous mixer) or
a batch mixer, polymeric foam can be produced. Supercritical carbon
dioxide, an environmentally friendly, low-cost, non-flammable, chemically
benign gas is used as the blowing agent. This process forms a
microcellular foam with very high cell density (>10.sup.9 cells/cc) and
small cell size (<5 microns) can be achieved by controlling the
CO.sub.2 content, melt and die temperature, and pressure drop rate.
Des particules de nano-sized telles que nano-clays peuvent être mélangées à des polymères par la fonte composant ou polymérisation in-situ. En modifiant la surface de particules avec des divers agents tensio-actifs et en commandant des états de traitement, nous pouvons réaliser intercalé (dispersion partielle) ou exfoliated (pleine dispersion) la distribution de nano-clay en polymères avec le contenu d'argile jusqu'à 35% en poids. Quand un agent de soufflage est injecté dans le nanocomposite dans une extrudeuse (un mélangeur continu) ou un mélangeur en lots, la mousse polymère peut être produite. L'anhydride carbonique supercritique, dans l'environnement un amical, peu coûteux, inflammable, gaz chimiquement bénin est employé comme agent de soufflage. Ce processus forme une mousse microcellulaire avec la densité très élevée de cellules (10.sup.9 cells/cc) et la petite taille de cellules (