There is provided a resin powder for molding which comprises 35 to 98% by
weight of a polytetrafluoroethylene powder having an average particle size
of not more than 120 .mu.m, 35 to 2% by weight of a heat resistant
aromatic polyoxybenzoyl ester resin powder subjected to water repelling
treatment and 30 to 0% by weight of an inorganic filler, has an apparent
density of not less than 0.6 g/cm.sup.3 and an average particle size of
not more than 800 .mu.m, and provides a molded article having an
elongation at break of not less than 20%. The resin powder for molding is
free from separation of a filler, has excellent flowability and apparent
density which are important characteristics in handling the powder, and
can provide a PTFE molded article having a high elongation which has not
been obtained.
Er verstrekt een harspoeder wordt voor het vormen die uit 35 tot 98% bij het gewicht van een polytetrafluoroethylene poeder bestaat dat een gemiddelde deeltjesgrootte van mu.m niet meer dan 120 heeft, 35 tot 2% bij het gewicht van een hittebestendig aromatisch de harspoeder van de polyoxybenzoylester dat aan water wordt onderworpen dat behandeling afweert en 30 tot 0% bij het gewicht van een anorganische vuller, heeft een duidelijke dichtheid van niet minder dan 0,6 g/cm.sup.3 en een gemiddelde deeltjesgrootte van mu.m niet meer dan 800, en verstrekt een gevormd artikel dat een verlenging heeft bij onderbreking van niet minder dan 20%. Het harspoeder voor het vormen is vrij van scheiding van een vuller, heeft uitstekende vloeibaarheid en duidelijke dichtheid die belangrijke kenmerken in de behandeling van het poeder zijn, en kan een PTFE gevormd artikel verstrekken dat een hoge verlenging heeft die niet is verkregen.