Proton conducting membranes having improved resistance to methanol
crossover are provided, along with methods for their manufacture. In a
preferred embodiment, the polymeric membranes are formed by (a) dissolving
a polymer, preferably a polyphosphazene, in an organic solvent to form a
polymer solution; (b) adding an oxyacid to the polymer solution; (c)
optionally, adding water to the polymer solution, preferably in a molar
ratio equivalent to the oxyacid; (d) optionally, concentrating the polymer
solution; (e) casting the polymer solution on a casting surface, such as
one formed of or coated with TEFLON.TM.; and (f) removing the organic
solvent, so as to form the polymeric membrane. A particularly useful
application for these polymeric membranes is in fuel cells, such as those
wherein methanol and oxygen are converted into electrical energy.
Het proton dat membranen leidt die weerstand tegen methanoloversteekplaats hebben verbeterd wordt verstrekt, samen met methodes voor hun vervaardiging. In een aangewezen belichaming, worden de polymere membranen gevormd door (a) een polymeer, bij voorkeur een polyphosphazene, in een organisch oplosmiddel op te lossen om een polymeeroplossing te vormen; (b) het toevoegen van oxyacid aan de polymeeroplossing; (c) dat naar keuze, water toevoegt aan de polymeeroplossing, bij voorkeur in een maalverhouding gelijkwaardig aan oxyacid; (d) dat naar keuze, de polymeeroplossing concentreert; (e) gietend de polymeeroplossing op een het gieten oppervlakte, zoals één gevormd van of met een laag bedekt met TEFLONTM.; en (f) verwijderend het organische oplosmiddel, om het polymere membraan te vormen. Een bijzonder nuttige toepassing voor deze polymere membranen is in brandstofcellen, zoals die waarin de methanol en de zuurstof in elektroenergie worden omgezet.