The invention provides a process for making a let-down of glass fiber
reinforced composite comprising a polymer matrix and from 5 wt. % to about
60 wt. % of reinforcing fibers long fibers. The fibers are incorporated in
the let-down as a concentrate of pultruded composite of substantially
parallel fibers and thermoplastic polyamide where fiber length equals
pellet length. The fibers in the let-down have improved dispersion and
orientation in the final thermoplastic polymer matrix thereby providing
substantially improved physical properties from the forming of the fiber
reinforced pellet with a modified pellet polymer matrix. The long fibers
are incorporated as a concentrate pellet in the final matrix polymer by
mixing pellets with the final polymer compound in a heated extrusion
mixing zone used to convey a composite melt into a shaping zone, whereby
the mixing under heat and rotational shear disperses the long
fiber-reinforced pellets into the let-down matrix polymer.
Вымысел снабубежит процесс для делать let-down смеси стекловолокна усиленной состоя из матрицы полимера и от 5 wt % около 60 wt % усиливать волокна волокон длиной. Волокна включены в let-down по мере того как шлих pultruded смесь существенн параллельных волокон и термопластикового полиамида где длина волокна приравнивает длина лепешки. Волокна в let-down улучшали рассеивание и ориентацию в окончательной термопластиковой матрице полимера таким образом обеспечивая существенн улучшенные физические свойства от формировать лепешки усиленной волокном с доработанной матрицей полимера лепешки. Длинние волокна включены по мере того как лепешка шлиха в окончательном полимере матрицы путем смешивать лепешки с окончательной смесью полимера в нагретой зоне штрангя-прессовани смешивая использовала транспортировать составной melt в формируя зону, whereby смешивать под жарой и вращательные ножницы разметали длинние fiber-reinforced лепешки в полимер матрицы let-down.