A method for producing an electric lamp having a vitreous lamp bulb and a
foil of molybdenum or a doped molybdenum alloy which is pinched in the
lamp bulb includes post-treating the unfinished foil such that
substantially non-contiguous, insular regions of material agglomerates are
formed. The material agglomerates are formed of molybdenum, molybdenum
alloys, titanium, silicon, an oxide, a mixed oxide and/or an oxidic
compound, with a vapor pressure of in each case less than 10 mbar at
2000.degree. C. The substantially non-contiguous, insular regions are
formed on at least 5 percent and at most 60 percent of the area of the
foil surface. In this way, the adhesive strength between the foil and the
glass and therefore also the service life of the lamp are significantly
improved.
Een methode om een elektrische lamp te produceren die een glaslampbol en een folie van molybdeen of een gesmeerde molybdeenlegering die heeft in de lampbol wordt geknepen omvat post-behandelt de onvolledige folie dusdanig dat de wezenlijk niet aangrenzende, insulaire gebieden van materiële agglomeraten worden gevormd. De materiële agglomeraten worden gevormd van molybdeen, molybdeenlegeringen, titanium, silicium, een oxyde, een gemengd oxyde en/of een oxidic samenstelling, met een dampdruk van in elk geval dan minder 10 mbar bij 2000.degree. C. De wezenlijk niet aangrenzende, insulaire gebieden worden gevormd op minstens 5 percent en hoogstens de meeste 60 percenten van het gebied van de folieoppervlakte. Op deze wijze, zijn de zelfklevende sterkte tussen de folie en het glas en daarom ook het de dienstleven van de lamp beduidend beter.