In a process of generating a polyurethane foam by forming a mixture
including isocyanate and polyol reactants, catalyst, and blowing agent,
which mixture reacts exothermically to yield a rigid polyurethane foam,
there is included in the mixture expandable polymer beads, made of a
thermoplastic polymer (e.g., polystyrene or a polyolefin) that has a
softening point at or below the maximum temperature reached during the
exothermic reaction. The beads may be added in unexpanded form, partially
expanded form, or fully expanded form. The heat of the urethane-forming
reaction causes the beads to sinter, creating hollow polymeric spheres in
the foam, which are larger than the cells in the polyurethane matrix, and
which appear to improve the foam's crush resistance.
En un proceso de generar una espuma del poliuretano formando una mezcla incluyendo los reactivo del isocianato y del polyol, el catalizador, y el agente que sopla, que la mezcla reacciona exotérmico para rendir a una espuma rígida del poliuretano, se incluye en los granos extensibles del polímero de la mezcla, hechos de un polímero termoplástico (e.g., poliestireno o un polyolefin) en el cual tenga un punto que ablanda o debajo de la temperatura máxima alcanzada durante la reacción exotérmica. Los granos se pueden agregar en forma sin dilatar, forma parcialmente ampliada, o forma completamente ampliada. El calor de la reacción de urethane-formacio'n hace los granos sinterizar, creando las esferas poliméricas huecos en la espuma, que son más grandes que las células en la matriz del poliuretano, y que aparecen mejorar la resistencia del agolpamiento de la espuma.