The invention relates to a thermoplastic membrane (e.g. film, fluid
barrier, and the like) which is formed from a blend of:
a) a first polymer component (FPC), wherein said FPC comprises a
propylene-ethylene copolymer containing from 80 to 93 percent by weight of
units derived from propylene, and having a melting point derived from
stereoregular polypropylene sequences, as determined by differential
scanning calorimetry (DSC), in the range of from 25.degree. C. to
70.degree. C., and a heat of fusion of from 2 J/g to 25 J/g;
b) an inorganic filler;
c) a processing oil, and
d) optionally, a second polymer component (SPC), wherein said SPC is a
stereoregular polypropylene containing less than 7 percent by weight of
units derived from ethylene or alpha-olefin monomer containing from 4 to 8
carbon atoms and having melting point, as determined by DSC, greater than
130.degree. C., and a heat of fusion greater than 80 J/g.
A invenção relaciona-se a uma membrana thermoplastic (por exemplo película, barreira fluida, e o gosto) de que seja dado forma de uma mistura: a) um primeiro componente do polímero (FPC), wherein FPC dito compreende um copolymer do propylene-etileno que contem 80 a 93 por cento pelo peso das unidades derivadas do propylene, e ter um ponto de derretimento derivado das seqüências stereoregular do polypropylene, como determinado pelo calorimetry de exploração diferencial (DSC), na escala de 25.degree. C. a 70.degree. C., e um calor da fusão de 2 J/g a 25 J/g; b) um enchimento inorgánico; c) um óleo processando, e d) opcionalmente, um segundo componente do polímero (SPC), wherein o SPC dito é um polypropylene stereoregular que contem menos de 7 por cento pelo peso das unidades derivadas do monomer do etileno ou do alceno alfa que contem 4 a 8 átomos de carbono e que tem o ponto de derretimento, como determinado por DSC, mais grande do que 130.degree. C., e um calor da fusão mais extremamente de 80 J/g.