The production of a cold-rolled strip or sheet of steel with good deforming
properties, which is subjected to recrystallizing annealing and, if
appropriate, a dressing operation after hot rolling, coiling and cold
rolling and has a bake-hardening potential after a subsequent deformation
and for a subsequent temperature treatment, succeeds because the
recrystallizing annealing is carried out in a bell-type furnace while
coiled and because the strip or sheet is subjected to cooling at a cooling
rate of .gtoreq.1.degree. C./s after the recrystallizing annealing from a
temperature T of 200.degree. C..ltoreq.T.ltoreq.A.sub.1. It is
consequently possible to obtain properties of bell-annealed steels and
nevertheless attain a bake-hardening effect, in particular for C contents
of .gtoreq.0.02%.
Die Produktion eines kaltgewalzten Streifens oder des Blattes des Stahls mit gutem, Eigenschaften verformend, das umkristallisierendem Ausglühen und unterworfen wird, wenn passend, einem ankleidenden, Betrieb nach heißem Rollen, umwickelnd und kaltes Rollen und hat ein backen-verhärtendes Potential nach einer folgenden Deformation und für eine folgende Temperaturbehandlung, folgt, weil das umkristallisierende Ausglühen in einem Haubenofen durchgeführt wird, wenn aufgerollt und weil der Streifen oder das Blatt dem Abkühlen mit einer abkühlenden Rate von gtoreq.1.degree unterworfen wird. C./s nach dem umkristallisierenden Ausglühen von einer Temperatur T von 200.degree. C..ltoreq.T.ltoreq.A.sub.1. Es ist folglich möglich, Eigenschaften der Glocke-getemperten Stahle zu erreichen und einen backen-verhärtenden Effekt, insbesondere für C Inhalt von gtoreq.0.02% dennoch zu erreichen.