A dielectric ceramic composition having high static capacitance and high
dielectric constant and satisfying X7R characteristics and a multilayer
ceramic capacitor using the same is provided. The dielectric ceramic
composition comprises barium titanate as a main component, and comprises
magnesium oxide, dysprosium oxide, barium oxide, calcium oxide, and
vanadium oxide, as subcomponents, wherein magnesium oxide converted into
MgO is 1 to 3 mol, dysprosium oxide converted into Dy.sub.2 O.sub.3 is 1
to 5 mol, total of barium oxide and calcium oxide converted into BaO and
CaO, respectively, is 0.1 to 5 mol, and vanadium oxide converted into
V.sub.2 O.sub.5 is 0.01 to 0.1 mol, when barium titanate converted into
BaTiO.sub.3 is 100 mol.
Een diëlektrische ceramische samenstelling die hoge statische capacitieve weerstand en hoge diëlektrische constante heeft en X7R kenmerken en een multilayer ceramische condensator tevredenstelt die het zelfde gebruikt wordt verstrekt. De diëlektrische ceramische samenstelling bestaat barium uit titanaat als hoofdcomponent, en bestaat magnesium uit oxyde, dysprosiumoxyde, bariumoxyde, calciumoxyde, en het vanadiumoxyde, als subcomponenten, waarin het magnesiumoxyde omgezet in MgO 1 tot 3 mol is, dysprosiumoxyde omgezet in Dy.sub.2 O.sub.3 is totaal 1 tot 5 mol, van bariumoxyde en calciumoxyde omgezet in BaO en CaO, respectievelijk, is 0,1 tot 5 mol, en het vanadiumoxyde omgezet in V.sub.2 O.sub.5 is 0,01 tot 0,1 mol, wanneer het bariumtitanaat omgezet in BaTiO.sub.3 100 mol is.