A Nickel free high manganese YW35 steel which has high strength and high
tenacity at low temperature, and a fishplate made of the same. The YW35
steel for steel rail fishplate is produced by adding a selected amount of
Molybdenum and microelement Vanadium and Niobium in a high Manganese steel
and reducing the carbon content thereof, to thereby improve the low
temperature property of the steel. The YW35 steel has (by weight
percentage): C: 0.32.about.0.40, MN: 1.10.about.1.30, Is: 0.30.about.0.50,
p: <0.035, S: <0.035, MO: 0.15.about.0.25, V: 0.06.about.0.20, NB:
0.04.about.0.07, Cu: <0.20, and a balancing amount of Fe.
Un acero alto libre del manganeso YW35 del níquel que tiene alta fuerza y alta tenacidad en la baja temperatura, y un fishplate hicieron igual. El acero YW35 para el fishplate de acero del carril es producido agregando una cantidad seleccionada de molibdeno y vanadio y niobium del microelemento en un acero alto del manganeso y reduciendo el contenido del carbón de eso, de tal modo para mejorar la característica de la baja temperatura del acero. El acero YW35 tiene (por porcentaje del peso): C: 0.32.about.0.40, MANGANESO: 1.10.about.1.30, es: 0.30.about.0.50, p: