The invention provides a high-carbon steel pipe having superior cold
workability and induction hardenability, and a method of producing the
steel pipe. The method comprises the steps of heating or soaking a base
steel pipe having a composition containing C: 0.3 to 0.8%, Si: not more
than 2%, and Mn: not more than 3%, and then carrying out reducing rolling
on the base steel pipe at least in the temperature range of (Ac.sub.1,
transformation point -50.degree. C.) to Ac.sub.1, transformation point
with an accumulated reduction in diameter of not less than 30%. A
structure in which the grain size of cementite is not greater than 1.0
.mu.m is obtained, thus resulting in improved cold workability and
induction hardenability.
L'invenzione fornisce un tubo d'acciaio ad alto tenore di carbonio che hanno hardenability freddo superiore di induzione e di workability e un metodo di produrre il tubo d'acciaio. Il metodo contiene i punti il heating o impregnare un tubo d'acciaio basso che ha una composizione contenere la C: 0.3 - 0.8%, silicone: non più di 2% e manganese: non più di 3% ed allora effettuare riducendo rolling sul tubo d'acciaio basso almeno nella gamma di temperature di (Ac.sub.1, punto -50.degree di trasformazione. C.) a Ac.sub.1, punto di trasformazione con una riduzione accumulata di diametro di 30%. Una struttura in cui il formato di grano di cementite non è più grande di il mu.m 1.0 è ottenuto, così con conseguente hardenability freddo migliorato di induzione e di workability.