A ferritic stainless steel sheet for use in automobile fuel tanks and fuel
pipes having smooth surface and resistance to organic acid is provided.
The sheet contains, by mass, not more than about 0.1% C, not more than
about 1.0 Si, not more than about 1.5 % Mn, not more than about 0.06% P,
not more than about 0.03% S, about 11% to about 23% Cr, not more than
about 2.0% Ni, about 0.5% to about 3.0% Mo, not more than about 1.0% Al,
not more than about 0.04% N, at least one of not more than about 0.8% Nb
and not more than about 1.0% Ti, and the balance being Fe and unavoidable
impurities, satisfying the relationship:
18.ltoreq.Nb/(C+N)+2Ti/(C+N).ltoreq.60, wherein C, N, Nb, and. Ti in the
relationship represent the C, N, Nb, and Ti contents by mass percent,
respectively. A process for making the same is also provided.
Ein ferritisches rostfreies Stahlblech für Gebrauch in den Automobilkraftstofftanks und in Kraftstoffrohren, die glatte Oberfläche haben und Widerstand zur organischen Säure wird zur Verfügung gestellt. Das Blatt enthält, durch Masse, nicht mehr als ungefähr 0.1% C, nicht mehr als ungefähr 1.0 Silikon, nicht mehr als ungefähr 1.5 % Mangan, nicht mehr als ungefähr 0.06% P, nicht mehr als ungefähr 0.03% S, ungefähr 11% zum ungefähr 23% Cr, nicht mehr als ungefähr 2.0% Ni, ungefähr 0.5% zu ungefähr 3.0% MO, nicht mehr als ungefähr 1.0% Al, nicht mehr als ungefähr 0.04% N, mindestens eins von nicht mehr als ungefähr 0.8% Notiz: und nicht mehr als Ti ungefähr 1.0% und die Balance, die F.E. und unvermeidbare Verunreinigungen ist und erfüllt das Verhältnis: 18.ltoreq.Nb/(C+N)+2Ti/(C+N).ltoreq.60, worin C, N, Notiz: und. Ti im Verhältnis stellt den C, N, Notiz: und Tiinhalt durch Massenprozente, beziehungsweise dar. Ein Prozeß für das Bilden dasselbe wird auch zur Verfügung gestellt.