Polycarbonate compositions incorporating long chain alkylphenol endgroups,
for example cardanol, show enhanced pit replication characteristics when
molded into optical disks. The enhancement in molding performance is
especially pronounced at the shortest mold cycle times tested. Thus, a
blend of 75 parts by weight bisphenol A polycarbonate 92 percent encapped
with phenol, and 25 parts by weight bisphenol A polycarbonate about 100
percent endcapped with cardanol showed enhanced pit replication
performance in optical disk molding trials relative to the same bisphenol
A polycarbonate alone and analogous blends utilizing short chain
alkylphenols.
Las composiciones del polycarbonate que incorporaban los endgroups con cadena larga del alkylphenol, por ejemplo cardanol, demostración realzaron características de la réplica del hoyo cuando estaban moldeadas en discos ópticos. El realce en funcionamiento del moldeado es especialmente pronunciado en las duraciones de ciclo más cortas del molde probadas. Así, una mezcla de 75 porciones por el polycarbonate del bisphenol A del peso 92 por ciento encapped con el fenol, y 25 porciones por el polycarbonate del bisphenol A del peso cerca de 100 por ciento endcapped con funcionamiento realzado demostrado cardanol de la réplica del hoyo en ensayos ópticos del moldeado del disco concerniente al mismo polycarbonate del bisphenol A solo y a las mezclas análogas que utilizaban los alkylphenols de cadena cortos.