High purity ammonium dimolybdate or molybdenum oxide is produced by the
pressure oxidation of low grade molybdenite concentrates or molybdenum
intermediates. The process entails nearly complete oxidation of the
sulfide minerals while optimizing the process chemistry and autoclave
conditions to solubilize as little of the molybdenum values as possible.
The autoclave discharge 12 is then subjected to a leaching step, either an
alkaline leach 50, 400 or ammonium leach 250 process, before or after a
liquid/solid separation step 20, 220, 410. The solution is then subjected
to (a) filtration 60, 410, solvent extraction 70, 440, crystallization
90,450, and calcination 120, 480 or (b) filtration 260, 280,
crystallization 290, and calcination 320 to produce a product suitable for
chemical-grade molybdenum oxide 125, 325, 485.
Το αμμώνιο υψηλής αγνότητας dimolybdate ή το οξείδιο μολυβδαίνιου παράγεται από την οξείδωση πίεσης molybdenite χαμηλού βαθμού των συμπυκνώσεων ή των μεσαζόντων μολυβδαίνιου. Η διαδικασία συνεπάγεται σχεδόν την πλήρη οξείδωση των μεταλλευμάτων σουλφιδίου βελτιστοποιώντας τους όρους χημείας και χυτρών πιέσεως διαδικασίας για να διαλυτοποιήσει όσο το δυνατόν περισσότερα των τιμών μολυβδαίνιου. Η απαλλαγή 12 χυτρών πιέσεως υποβάλλεται έπειτα σε ένα διυλίζοντας βήμα, είτε ένας αλκαλικός διαχωρισμός των μεταλλικών ενώσεων 50 ..400 είτε διαχωρισμός των μεταλλικών ενώσεων 250 αμμωνίου διαδικασία, πριν από είτε μετά από ένα υγρό/στερεό βήμα 20 ..220, 410 χωρισμού. Η λύση υποβάλλεται έπειτα (α) στη διήθηση 60 ..410, τη διαλυτική εξαγωγή 70 ..440, κρυστάλλωση 90.450, και calcination 120 ..480 ή (β) τη διήθηση 260, 280, την κρυστάλλωση 290, και calcination 320 για να παραγάγει ένα προϊόν κατάλληλο για το οξείδιο 125 ..325, 485 μολυβδαίνιου χημικός-βαθμού.