The invention relates to high strength aluminium--based alloy of
Al--Zn--Mg--Cu system and the articles made thereof. The present alloy is
characterized by the combination of improved properties: flowability,
technological plasticity, fracture toughness while preserving high levels
of strength properties.
Said alloy comprises (mass. %):
Zn 6.35-8.0 Si 0.01-0.2
Mg 0.5-2.5 Fe 0.06-0.25
Cu 0.8-1.3 Zr 0.07-0.2
Cr 0.001-0.05 Ti 0.03-0.1
Mn 0.001-0.1 Be 0.0001-0.05
and at least one element from the group of alkali-earth metals:
K 0.0001-0.01
Na 0.0001-0.01
Ca 0.0001-0.01
Al-balance
the sum Zr+2Ti.ltoreq.0.3%, and the ratio Si:Be.gtoreq.2.
The invented alloy is suitable for producing large-sized, extruded, rolled
and forged semiproduct articles used for manufacture of loaded members of
aircraft, cars and other machinery.
De uitvinding heeft op hoog sterktealuminium betrekking -- gebaseerde legering van Al -- Zn -- Mg -- het systeem van Cu en de daarvan gemaakte artikelen. De huidige legering wordt gekenmerkt door de combinatie betere eigenschappen: vloeibaarheid, technologische plasticiteit, breukhardheid terwijl het bewaren van hoge niveaus van sterkteeigenschappen. De bovengenoemde legering bestaat uit (Massachusetts %): Zn 6.35-8.0 Si 0.01-0.2 Mg 0.5-2.5 Fe 0.06-0.25 Cu 0.8-1.3 Zr 0.07-0.2 Cr 0.001-0.05 Ti 0.03-0.1 Mn 0.001-0.1 is 0.0001-0.05 en minstens één element van de groep alkali-aardemetalen: K 0.0001-0.01 Ca 0.0001-0.01 van Na 0.0001-0.01 al-Saldo som Zr+2Ti.ltoreq.0.3%, en de verhouding Si:Be.gtoreq.2. De uitgevonden legering is geschikt om grote, uitgedreven, gerolde en gesmede semiproduct artikelen te veroorzaken die voor vervaardiging van geladen leden van vliegtuigen, auto's en andere machines worden gebruikt.