A composite body of silicon carbide having binderless, allotropic carbon
granules distributed throughout is produced. The nominal size of the
binderless allotropic carbon granules can range from 5 to 500 micrometers.
The concentration of the binderless allotropic carbon particles can vary
from 1.0 to 35.0 weight percent. The process to produce such a composite
body is to sinter silicon carbide with binderless, carbon-yielding
precursor granules. The composite body is utilized in tribological
applications. The dense, impervious silicon carbide-binderless carbon
composite exhibits excellent physical and tribological characteristics
when used as a mechanical face seal, a sliding bearing arrangement, or
some other rubbing component.
Ein zusammengesetzter Körper des Silikonkarbids, welches die binderless, allotropic Carbonkörnchen gänzlich sich verteilen läßt, wird produziert. Die nominale Größe der binderless allotropic Carbonkörnchen kann von 5 bis 500 Mikrometer reichen. Die Konzentration der binderless allotropic Carbonpartikel kann von die Prozente mit 1.0 bis 35.0 Gewichten verändern. Der Prozeß, zum solch eines zusammengesetzten Körpers zu produzieren soll Silikonkarbid mit binderless sintern und Carbon-erbringt Vorläuferkörnchen. Der zusammengesetzte Körper wird in den tribological Anwendungen verwendet. Die dichte, undurchdringliche Silikon Karbid-binderless Carbonzusammensetzung stellt ausgezeichnete körperliche und tribological Eigenschaften aus, wenn sie als mechanische Gesicht Dichtung, gleitende Lageranordnung oder irgendein anderer Rubbingbestandteil verwendet wird.