The method for controlling flow pattern of molten steel in continuous
casting, comprises the steps of: (a) continuously casting a molten steel
injected through an immersion nozzle; (b) measuring temperatures of a
copper plate on longer side of the mold in width direction thereof at
plurality of points; (c) detecting a flow pattern of the molten steel in
the mold based on the time-sequential variations of temperatures of the
copper plate at individual measurement points; and (d) controlling the
flow pattern to establish a specified pattern on the basis of the detected
result. The temperatures of mold copper plate are measured by plurality of
temperature measurement elements buried in the rear face of the mold
copper plate for continuous casting. The temperature measurement elements
are arranged in a range of from 10 to 135 mm distant from the melt surface
in the mold in the slab-drawing direction.
Il metodo per il controllo del modello di flusso di acciaio fuso in colata continua, contiene i punti: (a) continuo colata un acciaio fuso iniettato attraverso un ugello di immersione; (b) temperature di misurazione di una piastra di rame dal lato più lungo della muffa nel senso di larghezza di ciò a pluralità di punti; (c) rilevando un modello di flusso dell'acciaio fuso nella muffa basata sulle variazioni tempo-sequenziali delle temperature della piastra di rame ai diversi punti di misura; e (d) controllando il modello di flusso per stabilire un modello specificato in base al risultato rilevato. Le temperature della piastra del rame della muffa sono misurate da pluralità di elementi di misura di temperatura sepolti nella faccia posteriore della piastra del rame della muffa per la colata continua. Gli elementi di misura di temperatura sono organizzati in una gamma distante di 10 - 135 millimetri dalla superficie della fusione nella muffa nel senso didisegno.