The present invention provides a grain-oriented silicon steel sheet
excellent in adhesiveness to tension-creating insulating coating films
formed on the grain-oriented silicon steel sheet produced by removing
inorganic mineral films composed of forsterite and so on with pickling or
the like or by deliberately preventing the formation thereof,
characterized by: having, at the interface between each of the
tension-creating insulating coating films and the steel sheet, an external
oxidation type membranous oxide film of 2 to 500 nm in average thickness
mainly composed of amorphous silica and/or a mixed oxide film consisting
of an external oxidation type membranous oxide film of 2 to 500 nm in
average thickness mainly composed of amorphous silica and particulate
oxides mainly composed of amorphous silica: and satisfying any one or more
of the specified requirements.
La présente invention fournit une tôle d'acier grain-orientée de silicium excellente dans l'adhérence aux films enduisants isolants tension-créants formés sur la tôle d'acier grain-orientée de silicium produite en enlevant les films minéraux inorganiques composés de forstérite et ainsi de suite avec mariner ou analogues ou en empêchant délibérément la formation en, caractérisé par : ayant, à l'interface entre chacun des films enduisants isolants tension-créants et la tôle d'acier, un type externe film membranous d'oxyde de 2 à 500 nm dans l'épaisseur moyenne principalement composée de silice amorphe et/ou un film mélangé d'oxydation d'oxyde se composant d'un type externe film membranous d'oxydation d'oxyde de 2 à 500 nm dans l'épaisseur moyenne principalement composée de silice amorphe et d'oxydes particulaires principalement composés de silice amorphe : et satisfaisant tout un ou plusieurs des conditions définies.