Precious metal values, particularly gold and silver, are liberated from
refractory, carbonate ores by adjusting the molar ratio of sulfide to
total acid consumers to between about 1.2 and about 3.2 in the ore feed to
a pressure oxidation process. The ore is contacted with oxygen to oxidize
sulfide in the ore with at least about 65 percent of the sulfide oxidation
occurring in a first oxidation zone at a temperature above about
360.degree. F. The oxidation of sulfide forms at least about 5 grams of
free sulfuric acid in the first oxidation zone. The oxidation process is
continued in subsequent oxidation zones. A gas stream is removed from the
oxidation zones and oxygen is separated from carbon dioxide and other
inerts in the gas stream and the purified oxygen is recycled to the
oxidation zones.
Des valeurs de métal précieux, en particulier or et argent, sont libérées du réfractaire, minerais de carbonate en ajustant le rapport molaire du sulfure sur des consommateurs d'acide total entre environ à 1.2 et environ 3.2 dans l'alimentation de minerai à un processus d'oxydation de pression. Le minerai est entré en contact avec l'oxygène pour oxyder le sulfure dans le minerai avec au moins environ 65 pour cent de l'oxydation de sulfure se produisant dans une première zone d'oxydation à une température au-dessus environ de 360.degree. F. L'oxydation du sulfure forme au moins environ 5 grammes d'acide sulfurique libre dans la première zone d'oxydation. Le processus d'oxydation est continué dans des zones suivantes d'oxydation. Un jet de gaz est enlevé des zones d'oxydation et l'oxygène est séparé de l'anhydride carbonique et d'autres inerts dans le gaz coulent et l'oxygène épuré est réutilisé aux zones d'oxydation.