A melt processable thermoplastic blend and a process for the preparation
thereof is disclosed. The blend comprises an intimate mixture of
polypropylene copolymer, EPDM and other additives and exhibits suitable
flow properties as well as mechanical properties (such as melt flow index:
10-15 g/10 minutes; flexural modulus: 8000-15000 kg/cm.sub.2 ; (notched
Izod impact strength: 50-60 kg.cm/cm; and heat deflection temperature:
60-105.degree. C.) necessary for injection molding of car bumpers as well
as their property requirements. It is prepared by extruding the components
in a twin screw extruder or a Buss co-kneader all together or in separate
batches, while for example, the twin screw temperature is maintained in
the range of 180 to 250.degree. C. and the screws are rotated at a speed
of 50 to 100 rpm.
Een smeltings verwerkbaar thermoplastisch mengsel en een proces voor de voorbereiding worden daarvan onthuld. Het mengsel bestaat uit een vertrouwelijk mengsel van polypropyleencopolymeer, EPDM en andere additieven en tentoongestelde voorwerpen geschikte stroomeigenschappen evenals mechanische eigenschappen (zoals de index van de smeltingsstroom: 10-15 g/10 notulen; flexural modulus: 8000-15000 kg/cm.sub.2; (ingekerfte schokweerstand Izod: 50-60 kg.cm/cm; en de temperatuur van de hitteafbuiging: 60-105.degree. C.) noodzakelijk voor injectie het vormen van autobumpers evenals hun bezitsvereisten. Het wordt voorbereid door de componenten in een tweeling samen alle schroefextruder of een mede-kneder Buss of in afzonderlijke partijen uit te drijven, terwijl bijvoorbeeld, de tweelingschroeftemperatuur in de waaier van 180 aan 250.degree. C. wordt gehandhaafd en de schroeven bij een snelheid van 50 tot 100 t/min worden geroteerd.