A resin composition comprising:
30 to 95 parts by weight of a biodegradable polylactic acid resin (A), and
70 to 5 parts by weight of a specified polyalkylene carbonate (B),
providing that the sum of components (A) and (B) is 100 parts by weight.
The invention provides an excellent resin composition which is
biodegradable, transparent, flexible and has gas barrier properties and
which is free from the occurrence of bleedout with the passage of time.
Further, the resin composition of the invention is excellent in
moldability, so that a variety of molded articles can be produced by
various molding techniques and put to practical use. The resultant molded
articles, when disposed of after use, exhibit high biodegradability in
natural environment.
Состав смолаы состоя из: от 30 до 95 частей by weight of biodegradable polylactic кисловочная смолаа (a), и от 70 до 5 частей by weight of определенный карбонат polyalkylene (b), обеспечивая что сумма компонентов (A) и (B) 100 частей весом. Вымысел обеспечивает превосходный состав смолаы biodegradable, прозрачны, гибки и имеют свойства барьера газа и который свободно от возникновения bleedout with the passage of time. Более потом, состав смолаы вымысла превосходн в moldability, так, что разнообразие отлитых в форму статьей сможет быть произведено различными методами прессформы и положить к практически пользе. Возникающие отлитые в форму статьи, после того как я размещаны after use, exhibit высокая биоразлагаемость в естественной окружающей среде.