A method for the preparation of nano size zinc oxide particles having an
average primary particle diameter of less than or equal to 15 nm, which
are redispersible in organic solvents and/or water, by basic hydrolysis of
at least one zinc compound in alcohol or an alcohol/water mixture. The
hydrolysis is carried out with substoichiometric amounts of base, based on
the zinc compound. The precipitate which originally forms during
hydrolysis is left to mature until the zinc oxide has completely
flocculated. This precipitate is then thickened to give a gel and
separated off from the supernatant phase.
Un método para la preparación de las partículas del óxido del cinc del tamaño del nano que tienen un diámetro primario medio de la partícula de menos que o del igual a 15 nm, que son redispersible en solventes orgánicos y/o riegan, por hidrólisis básica por lo menos de un compuesto del cinc en alcohol o una mezcla alcohol/water. La hidrólisis se realiza con las cantidades substoichiometric de base, basadas en el compuesto del cinc. El precipitado que forma originalmente durante la hidrólisis se deja para madurarse hasta que el óxido del cinc ha floculado totalmente. Este precipitado después se espesa para dar un gel y se separa apagado a partir de la fase flotante.