The process produces a stabilized zirconia powder by first contacting
zirconium basic carbonate particles with a stabilizer compound. This
reacts the zirconium basic carbonate particles with the stabilizer
compound through heterogeneous contact to form a stabilized zirconia
precursor. The stabilizer compound is for stabilizing a phase structure
selected from the group consisting of tetragonal phase, cubic phase and
mixtures of tetragonal and cubic phases. And calcining the stabilized
zirconia precursor removes gaseous by-products and forms the stabilized
zirconia powder. The stabilized zirconia powder has a phase structure
selected from the group consisting of tetragonal, cubic and mixtures of
tetragonal and cubic.
Der Prozeß produziert ein stabilisiertes zirconia Puder durch erste in Verbindung tretende grundlegende Karbonatpartikel des Zirkoniums mit einem Ausgleichermittel. Dieses reagiert die grundlegenden Karbonatpartikel des Zirkoniums mit dem Ausgleichermittel durch heterogenen Kontakt, um einen stabilisierten zirconia Vorläufer zu bilden. Das Ausgleichermittel ist für das Stabilisieren einer Phase Struktur, die von der Gruppe vorgewählt wird, die aus tetragonal Phase, Kubikphase und Mischungen von tetragonal und Kubikphasen besteht. Und das Kalzinieren des stabilisierten zirconia Vorläufers entfernt gasförmige Nebenerscheinungen und bildet das stabilisierte zirconia Puder. Das stabilisierte zirconia Puder hat eine Phase Struktur, die von der Gruppe vorgewählt wird, die aus tetragonal, Kubik und Mischungen von tetragonal und von Kubik besteht.