A high strength cold rolled steel sheet consists essentially of 0.0040 to
0.01% C, not more than 0.05% Si, 0.1 to 1.0% Mn, 0.01 to 0.05% P, not more
than 0.02% S, 0.01 to 0.1% sol.Al, not more than 0.004% N, 0.01 to 0.14%
Nb, by weight, and a balance of substantially Fe and inevitable
impurities, and having an n value of not less than 0.21 calculated from
two points (1% and 10%) of nominal strain determined by the uniaxial
tensile test, and a method for manufacturing the cold rolled steel sheet.
The high strength cold rolled steel sheet has excellent combined
formability, resistance to embrittlement during secondary operation,
formability at welded portions, and anti-burring performance, and has a
desirable surface appearance and uniformity of material in a coil, and
thus can be desirably used for automobile exterior panels.
Uma folha de aço rolada fria da força elevada consiste essencialmente em 0.0040 a 0.01% C, não mais de 0.05% silicone, 0.1 a 1.0% manganês, 0.01 a 0.05% P, não mais de 0.02% S, 0.01 a 0.1% sol.Al, não mais de 0.004% N, 0.01 a 0.14% Nb, pelo peso, e por um contrapeso substancialmente do Fe e de impurezas inevitáveis, e de ter um valor de n não mais menos de de 0.21 calculado de dois pontos (1% e 10%) da tensão nominal determinada pelo teste tensile uniaxial, e por um método para manufaturar a folha de aço rolada frio. A folha de aço rolada fria da força elevada tem o formability combinado excelente, a resistência ao embrittlement durante a operação secundária, o formability em parcelas soldadas, e o desempenho do anti-anti-burring, e tem uma aparência e uma uniformidade de superfície desejáveis do material em uma bobina, e assim pode desejàvel ser usada para os painéis do exterior do automóvel.