Iron oxide film directly grown on iron, steel, or other substrates by chemical or electrochemical oxidation is a promising material for energy storage through surface adsorption of static charges. As the electrode materials of energy-storage devices, the hydrated iron compound has a chemical composition of Fe.sub.x O.sub.y H.sub.z, where 1.0.ltoreq.x.ltoreq.3.0, 0.0.ltoreq.y.ltoreq.4.0, and 0.0.ltoreq.z.ltoreq.1.0. An aqueous or organic solution of a metallic salt including sulfates, sulfites, hydroxides, chlorides, phosphates and nitrates is used as electrolyte for the electrochemical devices. Cyclic voltammetry indicates that the iron-oxide electrodes in the electrolytes can store charges as high as 0.5 F/cm.sup.2 or 320 F/g of the electrode materials. Electrochemical capacitors using the iron oxide as the electrode material is an economical and viable power source for use in portable electronics, power tools, and electrical vehicles.

Проутюживите пленку окиси сразу, котор выросли на утюге, стали, или другие субстраты химически или электрохимической оксидацией будут перспективнейшим материалом для хранения энергии через поверхностную адсорбцию статических обязанностей. Как материалы электрода приспособлений energy-storage, ая водой смесь утюга имеет химическийа состав Fe.sub.x O.sub.y H.sub.z, где 1.0.ltoreq.x.ltoreq.3.0, 0.0.ltoreq.y.ltoreq.4.0, и 0.0.ltoreq.z.ltoreq.1.0. Водяное или органическое разрешение металлического соли включая сульфаты, сульфиты, окисоводоподы, хлориды, фосфаты и нитраты использовано как электролит для электрохимических приспособлений. Цикловая вольтамперометрия показывает что электроды утюг-okisi в электролитах могут хранить обязанности как высокие как 0.5 F/cm.sup.2 или 320 F/g материалов электрода. Электрохимические конденсаторы используя окись утюга как материал электрода будут экономичным и жизнеспособным источником питания для пользы в портативной электронике, електричюеских инструментах, и электрических кораблях.