The invention provides a process for the preparation of a thermoplastic elastomeric resin composition comprising melt kneading (a) 100 parts by weight of a block copolymer consisting of at least two polymeric blocks (A) composed mainly of a vinyl aromatic compound and at least one polymeric block (B) composed mainly of a conjugated diene compound, and/or a hydrogenated block copolymer obtained by hydrogenating said block copolymer, (b) 20 to 300 parts by weight of a non-aromatic softening agent for rubber, (c) 1 to 150 parts by weight of a peroxide-crosslinking type olefinic resin and/or a copolymeric rubber containing said resin, and (d) 10 to 150 parts by weight of a peroxide-decomposing type olefinic resin and/or a copolymer containing said resin, characterized in that the process comprises a step of heat-processing component (a), component (b), at least a part of component (c), at least a part of component (d) and at least a part of 1.0 to 1,200 parts by weight of component (e) in the presence of an organic peroxide to cause crosslinking, wherein component (e) is at least one thermoplastic polymer selected from the group consisting of polyester type (co)polymers, polyamide type (co)polymers and polyurethane type (co)polymers, and a subsequent step of blending these with the remaining part of component (c), and, the remaining part of component (d) and component (e), if any. The obtained composition is soft and excellent in heat deformation resistance and mechanical strength, moldability and processability, particularly in oil resistance and stain resistance.

A invenção fornece um processo para a preparação de uma composição elastomeric thermoplastic da resina que compreende o derretimento que kneading (a) 100 porções pelo peso de um copolymer do bloco que consiste ao menos em dois blocos polymeric (A) compostos principalmente de um composto aromatic do vinil e ao menos de um bloco polymeric (B) compostos principalmente de um composto conjugated do diene, e/ou um copolymer hydrogenated do bloco obtido hydrogenating o copolymer dito do bloco, peças pelo peso de um agente amaciando non-aromatic para a borracha, as peças peças de (b) 20 a 300 de (c) 1 a 150 pelo peso de um tipo peroxide-peroxide-crosslinking resina olefinic e/ou uma borracha copolymeric que contem resina dita, e de (d) 10 a 150 pelo peso de um tipo peroxide-peroxide-decomposing resina olefinic e/ou o copolymer que contem resina dita, caracterizada naquele o processo compreende uma etapa do componente do heat-processing (a), do componente (b), ao menos de uma parte do componente (c), ao menos de uma parte do componente (d) e ao menos de uma parte de 1.0 a 1.200 porções pelo peso do componente (e) na presença de um peroxide orgânico para causar crosslinking, wherein o componente (e) é ao menos um polímero thermoplastic selecionado do tipo consistindo do poliéster do grupo (co)polymers, tipo do polyamide (os co)polymers e o poliuretano datilografam (co)polymers, e uma etapa subseqüente de misturar estes com a parte restante do componente (c), e, restante a peça do componente (d) e do componente (e), se existerem. A composição obtida é macia e excelente na resistência da deformação do calor e força, moldability e processability mecânicos, particularmente na resistência do óleo e na resistência da mancha.