An aluminum alloy piping material for automotive piping excelling in corrosion resistance and workability and a method of fabricating the same. The aluminum alloy piping material is made of an aluminum alloy which contains 0.3-1.5% of Mn, 0.01-0.20% of Fe, and 0.01-0.20% of Si, wherein the content of Cu as impurities is limited to 0.05% or less, with the balance being Al and impurities, wherein, among Si compounds, Fe compounds, and Mn compounds present in the alloy's matrix, the number of compounds with a particle diameter (equivalent circle diameter, hereinafter the same) of 0.5 .mu.m or more is 3.times.10.sup.4 or less per mm.sup.2. The aluminum alloy piping material has a tensile strength of 70-130 MPa (temper: O material). An ingot of an aluminum alloy having the composition is hot extruded. The resulting extruded pipe is cold drawn at a working ratio of 30% or more and annealed.

Um material tranqüilo da liga de alumínio para o encanamento automotriz que excelling na resistência de corrosão e o workability e um método de fabricar o mesmo. O material tranqüilo da liga de alumínio é feito de uma liga de alumínio que contenha 0.3-1.5% do manganês, 0.01-0.20% do Fe, e 0.01-0.20% do silicone, wherein o índice do cu como impurezas é limitado a 0.05% ou mais menos, com o contrapeso que é al e impurezas, wherein, entre compostos do silicone, os compostos do Fe, e os compostos do manganês atuais na matriz, no número dos compostos com um diâmetro da partícula (diâmetro equivalente do círculo, em seguida o mesmo) de 0.5 mu.m ou em mais da liga são 3.times.10.sup.4 ou menos por mm.sup.2. O material tranqüilo da liga de alumínio tem uma força tensile de 70-130 MPa (têmpera: Material de O). Um ingot de uma liga de alumínio que tem a composição está quente expulso. A tubulação expulsa resultante é frio extraída em uma relação trabalhando de 30% ou mais e recozida.