The invention concerns a process for eliminating arsenic from a hydrocarbon
cut in which said cut is brought into contact with an absorption mass that
is at least partially pre-sulfurized and comprises a support and lead
oxide. The support, for example alumina, or said mass preferably has a
specific surface area in the range 10 to 300 m.sup.2 /g, a total pore
volume in the range 0.2 to 1.2 cm.sup.3 /g and a macroporous volume in the
range 0.1 to 0.5 cm.sup.3 /g. The lead content of said mass, expressed as
lead oxide, is preferably in the range of 5% to 50% by weight. The
fraction of the sulfurized mass preferably represents at least 1/20th of
the total volume of the absorption mass.
L'invention concerne un procédé pour éliminer l'arsenic d'un hydrocarbure coupé dedans quelle ladite coupe est mise en contact avec une masse d'absorption qui est pre-sulfurized au moins partiellement et comporte un appui et un oxyde de plomb. L'appui, par exemple alumine, ou ladite masse a de préférence une superficie spécifique dans le m.sup.2 de la gamme 10 à 300 /g, un volume total de pore dans le cm.sup.3 /g de la gamme 0.2 à 1.2 et un volume macroporeux dans le cm.sup.3 /g de la gamme 0.1 à 0.5. La teneur en plomb de ladite masse, exprimée comme l'oxyde de plomb, est de préférence dans la gamme de 5% à 50% en poids. La fraction du sulfurized la masse représente de préférence au moins le 1/20th de tout le volume de la masse d'absorption.