A part of a piston is composed of a metal matrix composite. The metal matrix composite is composed of a matrix of a light metal alloy and reinforcements formed of metallic fibers mixed in the matrix. The reinforcements are formed of an alloy that consists mainly of Fe and Cr and contains Al and/or Si. The Cr content and the Al and/or Si content of the reinforcements range from 5 to 30% and from 3 to 10%, respectively. The fiber diameter of the reinforcements ranges from .phi.20 .mu.m to .phi.100 .mu.m. The reinforcements are formed by the melt extraction method and have irregular peripheral surfaces. Solution-treatment of the metal matrix composite is carried out within a temperature range from 470.degree. C. to 500.degree. C. such that formation of intermetallic compounds is restrained.

Una parte di un pistone si compone di composto della tabella del metallo. Il composto della tabella del metallo si compone di tabella di una lega chiara e dei rinforzi del metallo formati delle fibre metalliche mescolate nella tabella. I rinforzi sono formati di una lega che è fatta di pricipalmente il Fe ed il Cr e contiene Al e/o il silicone. Il contenuto del Cr ed il contenuto nel silicone e/o in Al dei rinforzi variano da 5 a 30% e 3 - 10%, rispettivamente. Il diametro della fibra dei rinforzi varia dal mu.m del phi.20 al mu.m del phi.100. I rinforzi sono costituiti dal metodo dell'estrazione della fusione ed hanno superfici periferiche irregolari. il Soluzione-trattamento del composto della tabella del metallo è effettuato all'interno di una gamma di temperature da 470.degree. C. a 500.degree. C. tali che la formazione dei residui intermetallic è trattenuta.