A method for shifting the absorption peak wavelength in the wavelength range 900-1600 nm of an infrared radiation absorbing glass from less than 1100 nm to 1100 nm or longer without substantially changing the tint of the glass, comprising the step of irradiating with ultraviolet light of 400 nm or shorter at an energy density of 1.0.times.10.sup.6 J/m.sup.2 /hr or more to increase the content of FeO in the irradiated glass by reducing Fe (III) to Fe (II), the ultraviolet light irradiated glass thereby comprising 0.02 wt. % or more FeO in terms of Fe.sub.2 O.sub.3. The glass to be irradiated comprises, in % by weight: 65 to 80% SiO.sub.2, 0 to 5% Al.sub.2 O.sub.3, 0 to 10% MgO, 5 to 15% CaO, 10 to 18% Na.sub.2 O, 0 to 5% K.sub.2 O, 5 to 15% MgO+CaO, 10 to 20% Na.sub.2 O+K.sub.2 O, and 0 to 5% B.sub.2 O.sub.3 ; 0.02% or more total iron oxide (T-Fe.sub.2 O.sub.3) in terms of Fe.sub.2 O.sub.3, 0 to 2.0% CeO.sub.2, 0 to 1.0% TiO.sub.2, 0 to 0.005% CoO, and 0 to 0.005% Se.

Un metodo per spostare la lunghezza d'onda del picco di assorbimento nella lunghezza d'onda 900-1600 nm di un vetro assorbente di radiazione infrarossa più meno da nm di 1100 al nm 1100 o più lungo senza sostanzialmente cambiare la tinta del vetro, contenente il punto l'irradiazione con una luce ultravioletta di 400 nm o più corto ad una densità di energia di 1.0.times.10.sup.6 J/m.sup.2 /hr o più per aumentare il contenuto di FeO nel vetro irradiato riducendo il Fe (iii) al Fe (ii), la luce ultravioletta ha irradiato il vetro quindi che contiene 0.02 pesi % o più FeO in termini di Fe.sub.2 O.sub.3. Il vetro da irradiare contiene, in % di peso: 65 a 80% SiO.sub.2, a 0 al MgO di 5% Al.sub.2 O.sub.3, di 0 - di 10%, 5 a 15% cao, 10 a 18% Na.sub.2 O, 0 a 5% K.sub.2 O, 5 a 15% MgO+CaO, 10 a 20% Na.sub.2 O+K.sub.2 O e 0 a 5% B.sub.2 O.sub.3; ossido 0.02% o più totali del ferro (T-Fe.sub.2 O.sub.3) in termini di CeO.sub.2 di Fe.sub.2 O.sub.3, 0 - 2.0%, 0 - 1.0% TiO.sub.2, 0 - 0.005% coO e 0 - 0.005% Se.

 
Web www.patentalert.com

< Laminated transparency

< Method for producing air-quench-toughened glass plate

> Sizing compositions, methods and apparatus for cleaning sized fiber glass strands, yarns and fabrics

> Modified aminoplast crosslinkers and powder coating compositions containing such crosslinkers

~ 00083