A Mo source powder is added to and mixed with an iron-based powder containing 1.0% by mass or less of prealloyed Mn to yield a powder mixture containing 0.2 to 10.0% by mass of Mo, the resulting powder mixture is subjected to heat treatment in a reducing atmosphere to thereby yield an alloyed steel powder containing Mo as a powder partially diffused and bonded to a surface of the iron-based powder particles. The prepared alloyed steel powder for powder metallurgy has satisfactory compactability. The use of this alloyed steel powder can produce a sintered powder metal body (an intermediate material after compaction and preliminary sintering in re-compaction of sintered powder materials process) for highly strong sintered member.

Un polvo de la fuente del MES se agrega a y mezclado con un polvo hierro-basado contener 1.0% por la masa o el menos del prealloyed el manganeso para rendir una mezcla del polvo que contenía 0.2 a 10.0% por la masa del MES, la mezcla del polvo que resulta se sujeta al tratamiento de calor en una atmósfera reductora de tal modo para rendir un polvo de acero aleado que contiene el MES mientras que un polvo difundió y enlazó parcialmente a una superficie de las partículas hierro-basadas del polvo. El polvo de acero aleado preparado para la metalurgia del polvo tiene compactability satisfactorio. El uso de este polvo de acero aleado puede producir un cuerpo sinterizado del metal del polvo (un material intermedio después de la compactación y la sinterización preliminar en la re-compactacio'n del proceso sinterizado de los materiales del polvo) para el miembro sinterizado altamente fuerte.

 
Web www.patentalert.com

< Runflat tire with steel cord bead reinforcing layer

< Method of welding high chromium austenitic stainless steel pipe and shielding gas mixture for welding

> Enhanced machinability precipitation-hardenable stainless steel for critical applications

> Coated steel sheet and method for manufacturing the same

~ 00082