The present invention relates to a thermoplastic resin composition and a method for making the same. The composition comprises the reaction product of about 10 wt % to about 50 wt % polyphenylene ether, about 35 wt % to about 65 wt % polyamide, preferably about 0.4 wt % to about 3.0 wt % carbon fibrils, and optionally about 5 wt % to about 40 wt % talc, up to about 10 wt % compatibilizing agent and up to about 20 wt % impact modifier. The method comprises forming a carbon masterbatch with polyamide and introducing the masterbatch and the polyamide subsequent to compounding the polyphenylene ether with a compatibilizing agent.

La actual invención se relaciona con una composición termoplástica de la resina y un método para hacer igual. La composición abarca el producto de la reacción de cerca de 10 pesos % a % del éter del polyphenylene de cerca de 50 pesos, de cerca de 35 pesos % del polyamide de cerca de 65 pesos a %, de preferiblemente cerca de 0.4 peso % a % de las fibrillas del carbón de cerca de 3.0 pesos, y opcionalmente de cerca de 5 pesos % del talco de cerca de 40 pesos a %, hasta del agente compatibilizing de cerca de 10 pesos % y hasta % del modificante del impacto de cerca de 20 pesos. El método abarca la formación de un masterbatch del carbón con el polyamide e introducir el masterbatch y del polyamide subsecuente a componer el éter del polyphenylene con un agente compatibilizing.