Macrocellular polyolefin foams that can withstand temperatures above 110.degree. C. are described for use in sound absorption and insulation applications, especially in elevated temperature and/or moist environments. These foams have a large cell size (.gtoreq.1.5 mm), are open or closed-cell foams, and preferably have at least one perforation per square centimeter and/or a density less than 25 kg/m.sup.3. They are obtainable by extruding a high melt strength (HMS) polypropylene resin (PP), or preferably a blend of a HMS PP resin and a free radical polymerized ethylene polymer present in the blend in a weight ratio of at least 35:65, optionally another polymer such as a substantially random interpolymer, a cell size enlarging agent such a glycerol monostearate, an antioxidant, carbon black and/or flame retardant additives, using a volatile organic compound, e.g. isobutane, as blowing agent.

El polyolefin de Macrocellular hace espuma que puede soportar temperaturas sobre 110.degree. La C. se describe para el uso en usos sanos de la absorción y del aislamiento, especialmente en temperatura elevada y/o ambientes húmedos. Éstos hacen espuma tienen un tamaño de célula grande (gtoreq.1.5 milímetro), están abiertos o la cerrado-ce'lula hace espuma, y tiene preferiblemente por lo menos una perforación por centímetro cuadrado y/o una densidad menos de 25 kg/m.sup.3. Son obtenibles sacando una resina alta del polypropylene de la fuerza del derretimiento (HMS) (PP), o preferiblemente una mezcla de una resina del HMS PP y un radical libre polimerizó el polímero del etileno presente en la mezcla en un cociente del peso de por lo menos 35:65, opcionalmente otro polímero tal como un interpolymer substancialmente al azar, un agente de agrandamiento del tamaño de célula tal monostearate del glicerol, un antioxidante, un negro de carbón y/o los añadidos retardatarios de la llama, usando un compuesto orgánico volátil, e.g. isobutano, como agente que soplaba.