Steel strips and methods for producing steel strips are provided. In an illustrated embodiment, a method includes continuously casting molten low carbon steel into a strip of no more than 5 mm thickness having austenite grains that are coarse grains of 100-300 micron width; and providing desired yield strength in the cast strip by cooling the strip to transform the austenite grains to ferrite in a temperature range between 850.degree. C. and 400.degree. C. at a selected cooling rate of at least 0.01.degree. C./sec to produce a microstructure that provides a strip having a yield strength of at least 200 MPa. The low carbon steel produced desired microstructure.

As tiras e os métodos do aço para produzir as tiras de aço são fornecidos. Em uma incorporação ilustrada, um método inclui continuamente o aço de carbono baixo derretido da carcaça em uma tira de não mais de 5 milímetros de espessura que tem as grões do austenite que são grões grosseiras da largura do mícron 100-300; e fornecendo a força desejada do rendimento na tira do molde refrigerando a tira para transformar as grões do austenite ao ferrite em uma escala de temperatura entre 850.degree. C. e 400.degree. C. em uma taxa refrigerando selecionada ao menos de 0.01.degree. C./sec para produzir um microstructure que forneça uma tira que tem uma força do rendimento ao menos de 200 MPa. O aço de carbono baixo produziu o microstructure desejado.