This invention provides a process for making a nonwoven sheet of substantially continuous melt spun fibers by extruding melt spinnable polymer containing at least 30% by weight low IV poly(ethylene terephthalate), drawing the extruded fiber filaments at a rate of at least 6000 m/min, laying the fiber filaments down on a collection surface, and bonding the fiber filaments together to form a nonwoven sheet. The invention further provides a nonwoven sheet comprised of at least 30% by weight poly(ethylene terephthalate) having an intrinsic viscosity of less than 0.62 dl/g, where the sheet has a basis weight of less than 125 g/m.sup.2, and a grab tensile strength of at least 0.7 N/(g/m.sup.2).

Questa invenzione fornisce un processo per fare un foglio non tessuto delle fibre filate fusione sostanzialmente continua dal polimero spinnable sporgentesi della fusione che contiene almeno 30% di peso tereftalato basso del poly(ethylene del dispositivo di venipunzione), disegnante i filamenti sporti della fibra ad un tasso almeno di 6000 m/min, ponente i filamenti della fibra giù su una superficie dell'accumulazione e legante insieme i filamenti della fibra per formare un foglio non tessuto. L'invenzione ulteriore fornisce un foglio non tessuto formato almeno da 30% di peso tereftalato del poly(ethylene) che ha una viscosità intrinseca di più meno di 0.62 dl/g, dove il foglio ha un peso di base di più meno di 125 g/m.sup.2 e una resistenza alla trazione della gru a benna almeno di 0.7 N/(g/m.sup.2).