A method for the manufacture of steel products and products thus produced, wherein steel is subjected to precipitation hardening in a martensitic structure subsequent to soft annealing and thereafter shaping. The method steps include shaping followed by solution annealing between 1200.degree. C. and 1050.degree. C., quenching from the solution annealing temperature with a quenching speed of at least 5.degree. C. per second to a temperature below 500.degree. C., subjecting said steel to an isothermal martensitic transformation and subsequently hardening the steel at a temperature between 450.degree. C. and 550.degree. C. to precipitate particles out from solution into said martensitic structure.

Un método para la fabricación de los productos de acero y de los productos produjo así, en donde el acero se sujeta a la precipitación que endurece en una estructura martensitic subsecuente al recocido suave y que forma después de eso. Los pasos del método incluyen formar seguido por el recocido de la solución entre 1200.degree. C. y 1050.degree. C., apagando de la temperatura del recocido de la solución con una velocidad que apaga por lo menos de 5.degree. C. por segundo a una temperatura debajo de 500.degree. C., acero dicho que sujeta a una transformación martensitic isotérmica y posteriormente a endurecer el acero en una temperatura entre 450.degree. C. y 550.degree. C. para precipitar partículas hacia fuera de la solución en la estructura martensitic dicha.