An anionic surfactant having a thermal weight loss initiation temperature of at least 250.degree. C. is incorporated with a thermoplastic resin comprising a graft copolymer formed by graft-polymerizing an ethylenically unsaturated monomer onto a rubber trunk polymer obtained by emulsion polymerization using a carboxylic acid-type surfactant. As a result, it is possible to obtain an antistatic resin composition which can be effectively produced on an industrial scale and can provide a shaped product excellent in permanent antistatic property and free from haze or discoloration even when processed under severe processing conditions.

Um surfactant anionic que tem uma temperatura térmica da iniciação da perda do peso ao menos de 250.degree. O C. é incorporado com uma resina thermoplastic que compreende um copolymer do graft dado forma graft-polimerizando um monomer ethylenically unsaturated em um polímero de borracha do tronco obtido pela polimerização do emulsion usando um ácido-tipo carboxylic surfactant. Em conseqüência, é possível obter uma composição antiestática da resina que possa eficazmente ser produzida em uma escala industrial e pode fornecer um produto dado forma excelente na propriedade antiestática permanente e livrá-lo do embaçamento ou da descoloração mesmo quando processado sob circunstâncias processando severas.

 
Web www.patentalert.com

< Detergent tablet

< Radio frequency (RF) heating system

> Process for preparing azo colorants

> Olefinic thermoplastic elastomer composition and method for producing the same

~ 00062