A delayed fracture is effectively prevented by appropriately setting a shape and working stress, and working environment of a high strength member having more than 1,000 MPa of tensile strength. For this end, the relationship between a maximum value of diffusible hydrogen contents of unfailed specimens (H.sub.c) and Weibull stress are found and the content of diffusible hydrogen entered into steel from the environment due to corrosion during the use of the steel member (H.sub.e) is also found. Then, Weibull stress in the H.sub.c that is equal to the H.sub.e is found, thus determining the shape and working stress of the steel member so as to provide stress below the Weibull stress.

Uma fratura atrasada é impedida eficazmente apropriadamente pelo ajuste de um stress da forma e de funcionamento, e pelo ambiente de funcionamento de um membro elevado da força que tem mais de 1.000 MPa da força tensile. Para esta extremidade, o relacionamento entre um valor máximo de índices diffusible do hidrogênio de unfailed os espécimes (H.sub.c) e o stress de Weibull é encontrado e o índice do hidrogênio diffusible incorporado no aço do ambiente devido à corrosão durante o uso do membro de aço (H.sub.e) é encontrado também. Então, o stress de Weibull no H.sub.c que é igual ao H.sub.e é encontrado, assim determinando o stress da forma e de funcionamento do membro de aço para fornecer o stress abaixo do stress de Weibull.

 
Web www.patentalert.com

< Cold workable steel bar or wire and process

< Method of making a high-strength low-alloy hot rolled steel

> Method and apparatus for improving internal quality of continuously cast steel sections

> Method for producing load-optimized steel strips

~ 00062