A lithium secondary battery capable of improving high temperature cycle life characteristic effectively without decreasing discharge capacity. Amorphous carbon powder with a specific surface area of 10.0 m.sup.2 /g and a mean particle diameter of 7.0 .mu.m is used as negative electrode active material and lithium manganate with a Li/Mn ratio of 0.58 is used as positive electrode active material. Since a surface area of the negative electrode active material layer is made large by setting the mean particle diameter of the amorphous carbon powder to 10 .mu.m or less, the surface area of the negative electrode active material layer is sufficiently large that, even when inert coating is formed on the surface of the negative electrode due to manganese deposition caused by manganese elution from the positive electrode, high temperature cycle life characteristic can be improved without high temperature deterioration.

Uma bateria secundária do lítio capaz de melhorar a característica elevada da vida do ciclo da temperatura eficazmente sem capacidade diminuindo da descarga. O pó amorfo do carbono com uma área de superfície específica de 10.0 m.sup.2 /g e um diâmetro médio da partícula do mu.m 7.0 é usado como o material ativo do elétrodo negativo e o manganate do lítio com uma relação de Li/Mn de 0.58 é usado como o material ativo do elétrodo positivo. Desde uma área de superfície de elétrodo negativo a camada material ativa é feita grande ajustando o diâmetro médio da partícula do pó amorfo do carbono ao mu.m 10 ou menos, a área de superfície do elétrodo negativo a camada material ativa é suficientemente grande aquela, mesmo quando o revestimento inerte for dado forma na superfície do elétrodo negativo devido ao deposition do manganês causado pelo elution do manganês do elétrodo positivo, que característica de alta temperatura da vida do ciclo pode ser melhorado sem deterioração de alta temperatura.