A substrate and a target are disposed within a vacuum chamber, and an oxygen partial pressure within the vacuum chamber is set to 1.times.10.sup.-5 or less. Under this condition, a spinel ferrite thin film selected from the group consisting of compounds represented by the formula AE.sub.1+t Fe.sub.2-2t TM.sub.t O.sub.4, where AE represents an alkaline earth metal or an alkali metal, TM represents a transition metal and t falls within a range of between 0.2 and 0.6, and compounds represented by the formula Zn.sub.1-x Co.sub.x Fe.sub.2 O.sub.4, where x falls within a range of between 0.2 and 0.7, is deposited on the substrate by laser beam deposition. The particular method makes it possible to provide a spinel ferrite thin film realizing a spin glass state under temperatures around or higher than room temperature and capable of controlling the spin state by light.

Un substrat et une cible sont disposés dans une chambre de vide, et une pression partielle de l'oxygène dans la chambre de vide est placée à 1.times.10.sup.-5 ou moins. Dans cette condition, une couche mince de ferrite à spinelle choisie dans le groupe les composés représentés par la formule AE.sub.1+t Fe.sub.2-2t TM.sub.t O.sub.4, où AE représente un métal alcalinoterreux ou un métal alcalin, TM représente un métal de transition et t fait partie d'une marge de entre 0.2 et 0.6, et des composés représentés par la formule Zn.sub.1-x Co.sub.x Fe.sub.2 O.sub.4, où x fait partie d'une marge de entre 0.2 et 0.7, est déposés sur le substrat par le dépôt de rayon laser. La méthode particulière permet pour fournir une couche mince de ferrite à spinelle réalisant un état de verre de rotation sous les températures la température et capable autour ou plus haut qu'ambiantes de commander l'état de rotation par la lumière.