Powder coating compositions for metal substrates, a method of powder coating a metal substrate, and a metal article are disclosed. The powder coating composition is a thermoplastic material and comprises: (a) a first polyester having a weight average molecular weight of about 10,000 to about 80,000 and a Tg of greater than 45.degree. C. to about 100.degree. C., (b) a second polyester having a weight average molecular weight of about 10,000 to about 70,000 and a Tg of about -10.degree. C. to about 45.degree. C., and optionally, (c) a modifying resin, such as an epoxy resin having an epoxy equivalent weight of about 500 to about 15,000, wherein the Tg of the first and second polyesters differ by about 5.degree. C. to about 60.degree. C. The powder coating composition is applied to a metal substrate to provide a composition film having a thickness of about 1 to about 200 microns.

De de deklaagsamenstellingen van het poeder voor metaalsubstraten, een methode van poeder dat een metaalsubstraat met een laag bedekt, en een metaalartikel worden onthuld. De samenstelling van de poederdeklaag is een thermoplastisch materiaal en bestaat uit: (a) een eerste polyester die een gewichts gemiddeld moleculegewicht van ongeveer 10.000 aan ongeveer 80.000 en een Tg van groter heeft dan 45.degree. C. aan ongeveer 100.degree. C., (b) een tweede polyester die een gewichts gemiddeld moleculegewicht van ongeveer 10.000 aan ongeveer 70.000 en een Tg van ongeveer -10.degree. C. heeft aan ongeveer 45.degree. C., en naar keuze, (c) een het wijzigen zich hars, zoals een epoxyhars die een epoxy gelijkwaardig gewicht van ongeveer 500 heeft aan ongeveer 15.000, waarin Tg van de eerste en tweede polyesters door ongeveer 5.degree. C. aan ongeveer 60.degree. C verschilt. De samenstelling van de poederdeklaag wordt aangebracht op een metaalsubstraat om een samenstellingsfilm te verstrekken die een dikte van ongeveer 1 heeft aan ongeveer 200 microns.