The present invention provides a porous titania, which has an anatase-form crystalline structure, an anatase-form crystallite diameter of 3 nm to 10 nm, a degree of anatase crystallinity of 60% or more, a BET specific surface area of 10 m.sup.2 /g or more, a total pore volume of 0.05 cm.sup.3 /g or more, and a volume for pores having a pore radius of 1 nm or more of 0.02 cm.sup.3 /g or more, and the porous titania and the catalyst comprising the porous titania of the present invention exhibit an excellent catalytic activity for removal of nitrogen oxides, oxidation of organic substances, decomposition of dioxine compounds, as well as decomposition and removal of organic solvents, agricultural chemical and surfactant.

La actual invención proporciona un titania poroso, que tiene una estructura cristalina de la anatase-forma, un diámetro del cristalito de la anatase-forma de 3 nm a 10 nm, un grado de cristalinidad del anatase de el 60% o más, un área superficial específica de la APUESTA de 10 m.sup.2 /g o más, un volumen total del poro de 0.05 cm.sup.3 /g o más, y un volumen para los poros que tienen un radio del poro de 1 nm o más de 0.02 cm.sup.3 /g o más, y el titania poroso y el catalizador que abarcan el titania poroso del actual objeto expuesto de la invención una actividad catalítica excelente para el retiro de los óxidos del nitrógeno, oxidación de sustancias orgánicas, descomposición de los compuestos de la dioxina, así como la descomposición y retiro de solventes orgánicos, del producto químico agrícola y del surfactant.