Phenylethynyl containing reactive additives were prepared from aromatic diamines containing phenylethynyl groups and various ratios of phthalic anhydride and 4-phenylethynylphthalic anhydride in glacial acetic acid to form the imide in one step or in N-methyl-2-pyrrolidinone to form the amide acid intermediate. The reactive additives were mixed in various amounts (10% to 90%) with oligomers containing either terminal or pendent phenylethynyl groups (or both) to reduce the melt viscosity and thereby enhance processability. Upon thermal cure, the additives react and become chemically incorporated into the matrix and effect an increase in crosslink density relative to that of the host resin. This resultant increase in crosslink density has advantageous consequences on the cured resin properties such as higher glass transition temperature and higher modulus as compared to that of the host resin.

Phenylethynyl die reactieve additieven bevat werd van aromatische diaminen voorbereid phenylethynylgroepen en diverse verhoudingen van phthalic anhydride bevatten en 4-phenylethynylphthalic anhydride die in ijzig azijnzuur om de imide in één stap of in n-methyl-2-Pyrrolidinone te vormen om de amide zure tussenpersoon te vormen. De reactieve additieven werden gemengd in diverse bedragen (10% tot 90%) met oligomers die of eind of pendent phenylethynylgroepen (of allebei bevatten) om de smeltingsviscositeit te verminderen en daardoor werkbaarheid te verbeteren. Op thermische behandeling, reageren de additieven en worden die chemisch in de matrijs worden opgenomen en voeren een verhoging van kruisverbindingsdichtheid met betrekking tot uit dat van de gastheerhars. Deze resulterende verhoging van kruisverbindingsdichtheid heeft voordelige gevolgen op de genezen harseigenschappen zoals de hogere temperatuur van de glasovergang en hogere modulus in vergelijking tot dat van de gastheerhars.