A method for processing ultra-high molecular weight polyethylene (UHMWPE) of at least 400,000 by heating under an elevated pressure, followed by cooling, wherein UHMWPE having a lamellar thickness <12 nm and a melting temperature at atmospheric pressure >141.degree. C. is used, by carrying out the heating under an elevated pressure via a transient hexagonal phase, which phase is represented by the hatched area in the Figure, which lies below the equilibrium line of the phase transition orthorhombic phase--liquid phase, which area is enclosed by points (P.sub.1, T.sub.1 '), (P.sub.2, T.sub.1 '), (P.sub.2, T.sub.2) and (P.sub.1, T.sub.1 ), wherein T.sub.1 and T.sub.2 represent the equilibrium temperatures associated with pressures P.sub.1 and P.sub.2 respectively, followed by heating to melting and cooling to ambient temperature.

Un metodo per l'elaborazione del polietilene ultraelevato del peso molecolare (UHMWPE) almeno di 400.000 riscaldando sotto una pressione elevata, seguito raffreddandosi, in cui UHMWPE che ha uno spessore lamellare 141.degree. Il C. è usato, effettuando il heating sotto una pressione elevata via una fase esagonale transitoria, che la fase è rappresentata dalla zona covata nella la figura, che si trova sotto la linea di equilibrio della fase orthorhombic di transizione di fase -- fase liquida, che la zona è acclusa dai punti (P.sub.1, T.sub.1 '), (P.sub.2, T.sub.1 '), (P.sub.2, T.sub.2) e (P.sub.1, T.sub.1), in cui T.sub.1 e T.sub.2 rappresentano le temperature di equilibrio connesse con le pressioni P.sub.1 e P.sub.2 rispettivamente, è seguito riscaldando alla fusione ed al raffreddamento alla temperatura ambientale.

 
Web www.patentalert.com

< (none)

< Polyamide-imide having head-to-tail backbone

> Method of preparing molding compositions with fiber reinforcement and products obtained therefrom

> (none)

~ 00041