A method for making a consolidated wood product comprising coating wood components with a B-stageable, phenol-formaldehyde resole resin; heating the coated wood components to about 80 to 140.degree. C. for a time sufficient to advance the resin to a B-stage; forming a mat or stack of the wood components coated with the B-stage resin; exposing the mat or stack of coated wood components to a saturated or superheated steam atmosphere in a hot press; and compressing the layup to form the consolidated wood product. The phenol-formaldehyde resole resin used in the method has a number average molecular weight of between about 200 and 600, has a F:P mole ratio of about 1.3:1 to 2.0:1, and has been modified with 0 to about 5.5 wt % of caustic based on resin solids.

Une méthode pour faire un produit en bois consolidé comportant les composants en bois enduisants avec un B-stageable, résine de résol de phénol-formaldehyde ; chauffage des composants en bois enduits environ à 80 à 140.degree. C. pendant un certain temps suffisamment pour avancer la résine à une B-étape ; la formation d'une natte ou d'une pile des composants en bois a enduit de la résine d'B-étape ; exposer la natte ou la pile de composants en bois enduits à une atmosphère saturée ou surchauffée de vapeur dans une pression chaude ; et comprimant le layup pour former le produit en bois consolidé. La résine de résol de phénol-formaldehyde utilisée dans la méthode a un poids moléculaire de moyenne de nombre de entre environ 200 et 600, a un rapport molaire de F:P environ de 1.3:1 à 2.0:1, et a été modifiée avec 0 à environ 5.5 poids % de caustique basé sur des solides de résine.