In order to conduct welding so that the welded steel shows a decreased residual stress after welding without a post treatment such as a PWHT, the steel for welded structures and the welding wire of the present invention starts a transformation from austenite into martensite at a temperature (Ms temperature) from at least 200.degree. C. to up to 350.degree. C., and has a yield strength from at least 60 kg/mm.sup.2 to up to 120 kg/mm.sup.2 at the transformation starting temperature. The multipass welding process of the present invention comprises forming a weld metal having a Ms temperature of 150.degree. C. to 300.degree. C., and TIG remelt-run welding the surface of the final layer.

Afin de conduire la soudure de sorte que l'acier soudé montre un effort résiduel diminué après soudure sans traitement de poteau tel qu'un PWHT, l'acier pour les structures soudées et le fil de soudure de la présente invention engage une transformation à partir d'austenite dans le martensite à une température (la température de mme.) à partir au moins de 200.degree. C. à jusqu'à 350.degree. Le C., et a une force de rendement au moins de 60 kg/mm.sup.2 à jusqu'à 120 kg/mm.sup.2 à la température commençante de transformation. Le procédé à multipassage de soudure de la présente invention comporte former un métal de soudure ayant une température de mme. de 150.degree. C. à 300.degree. Le C., et le TIG refondre-courent souder la surface de la couche finale.

 
Web www.patentalert.com

< (none)

< Method for the co-deposition of silicon and nitrogen on stainless steel surface

> Non-oriented electromagnetic steel sheet having reduced magnetic anisotropy in high frequency region and excellent press workability

> (none)

~ 00040