A process for making steel in an electric arc furnace includes providing a molten charge which is a melt composed of a high carbon ferrous metal in the electric arc furnace by one of preparing the melt in the furnace or introducing the melt into the furnace, the high carbon ferrous metal being composed of less than 3% carbon, less than 0.2% silicon, and less than 0.2% manganese, and the melt having a temperature of at least 1375.degree. C.; adding to the molten charge provided in the furnace a solid metallic charge composed of least one material selected from the group consisting of scrap steel, hot briquetted iron, direct reduced iron, and iron ore to provide a charge mixture; refining the charge mixture by melting in the absence of gaseous oxygen to provide a molten steel; and superheating, finishing and tapping the molten steel into a ladle for subsequent casting thereof.

Μια διαδικασία για το χάλυβα σε έναν φούρνο ηλεκτρικών τόξων περιλαμβάνει την παροχή μιας λειωμένης δαπάνης που είναι ένα λειωμένο μέταλλο που αποτελείται από ένα υψηλό σιδηρούχο μέταλλο άνθρακα στο φούρνο ηλεκτρικών τόξων από μια από την προετοιμασία του λειωμένου μετάλλου στο φούρνο ή την εισαγωγή του λειωμένου μετάλλου στο φούρνο, το υψηλό σιδηρούχο μέταλλο άνθρακα που αποτελούνται από τον άνθρακα λιγότερο από 3%, πυρίτιο λιγότερο από 0,2%, και μαγγάνιο λιγότερο από 0,2%, και το λειωμένο μέταλλο που έχει μια θερμοκρασία τουλάχιστον 1375.degree. C.; η προσθήκη στη λειωμένη δαπάνη παρείχε στο φούρνο μια στερεά μεταλλική δαπάνη που αποτελείται από λιγότερο ένα υλικό που επιλέχτηκε από την ομάδα που αποτελείται από το χάλυβα απορρίματος, καυτός ο σίδηρος, ο άμεσος μειωμένος σίδηρος, και το μετάλλευμα σιδήρου για να παρέχει ένα μίγμα δαπανών καθαρισμός του μίγματος δαπανών με την τήξη ελλείψει του αεριώδους οξυγόνου για να παρέχει έναν λειωμένο χάλυβα και υπερθερμαίνοντας, τελειώνοντας και τρυπώντας το λειωμένο χάλυβα σε μια κουτάλα για την επόμενη ρίψη επ' αυτού.